Stainless Steel 420 Plates

Stainless Steel 420 Plates Specification

Diameter
Not applicable (Plate form)

Size
Standard: 1000mm x 2000mm, 1220mm x 2440mm, 1250mm x 2500mm, custom sizes available

Heat Resistance
Yes

Corrosion Resistant
Yes, moderate corrosion resistance

Hardness
50 HRC (Maximum, after hardening)

Product Form
Flat Plate / Sheet

Recyclable
Yes

Tensile Strength
min 700 MPa, up to 880 MPa

Coating Type
Uncoated, can be supplied with protective film

Material Composition %
Cr: 12-14%, C: 0.15-0.40%, Mn: 1%, Si: 1%, P: 0.04%, S: 0.03%

Product Name
Stainless Steel 420 Plates

Steel Type
Stainless Steel

Steel Product Type
Plate

Grade
420

Thickness
0.5mm to 100mm

Shape
Rectangular / Square / Custom Cut

Steel Standard
ASTM A240, EN 10088-2, JIS G4304

Surface
Bright, Polished, 2B, BA, No.1, No.4

Composition
High Chromium (12-14%), Carbon (0.15-0.40%)

Application
Industrial, Construction, Automotive, Cutlery, Surgical Instruments, Tools Manufacturing

Dimension (L*W*H)
Customizable as per requirement

Weight
Varies as per dimension

Color
Silver / Metallic

Material Grade
AISI 420

Finish Type
2B, Mirror, Matte, No.1, No.4

Usage
Cutlery, Surgical & Medical Instruments, Moulds, Valves, Gears, Construction

Forming
Good formability in annealed condition

Magnetic Properties
Magnetic in annealed and hardened conditions

Delivery Condition
Annealed / Hardened & Tempered / Pickled / Polished

Machinability
Good machinability in annealed condition

MOQ
As per supplier policy

Edge Condition
Mill edge / Slit edge

Density
7.75 g/cm³

Elongation
15% min (in 50 mm)

Weldability
Fair, needs special electrodes and pre/post weld heating

Modulus of Elasticity
200 GPa

Stainless Steel 420 Plates Trade Information

Minimum Order Quantity
100 Kilograms

Delivery Time
10-15 Days

About Stainless Steel 420 Plates

Stainless Steel 420 Plates boast unmatchable strength and commanding durability, making them a terrific choice for industries demanding reliability. Manufactured to ASTM A240, EN 10088-2, and JIS G4304 standards, these plates feature a high chromium content for moderate corrosion resistance and excellent heat resistance up to 650C. With customizable dimensions and competitive pricing, procurement is seamless and flexible. Good machinability and formability in the annealed condition allow for advance purchase planning. MOQ and delivery conditions are tailored to supplier policy, catering to construction, automotive, surgical, and tool manufacturing sectors.

Applications and Directions for Use

Stainless Steel 420 Plates are extensively used in cutlery, surgical instruments, automotive components, industrial tools, moulds, and construction projects. Designed for areas requiring moderate corrosion resistance and high tensile strength, these plates excel in demanding environments. For optimal results, utilize proper handling techniques, ensure correct preheating and electrode selection during welding, and choose the appropriate delivery condition. Users are advised to select the right thickness and surface finish based on the site's operational requirements.

Delivery, Payment, and Export Markets

Goods transport and freight logistics for Stainless Steel 420 Plates are efficiently managed, ensuring swift and safe exchange of materials. Delivery time is contingent on the specification and size, with most orders processed for quick dispatch. Payment terms typically align with supplier policy, accommodating advance purchase or exchange-based arrangements. Main export markets include India and several international regions where demand is robust, facilitated by established exporter, supplier, and wholesaler networks.

FAQ's of Stainless Steel 420 Plates:

Q: How should Stainless Steel 420 Plates be procured for industrial use?

A: Stainless Steel 420 Plates can be procured directly from manufacturers, exporters, or wholesalers by specifying required dimensions, surface finish, and delivery conditions. Minimum order quantities and procurement timelines are set by the supplier.

Q: What are the main benefits of using 420 grade stainless steel plates in construction and manufacturing?

A: The main benefits include commanding hardness, terrific machinability in the annealed condition, resistance to moderate corrosion, and adaptability for forming and custom cutting, making them highly sought-after for industrial and automotive components.

Q: Where are Stainless Steel 420 Plates most commonly applied?

A: These plates find application in diverse areas such as industrial manufacturing, construction, the automotive sector, cutlery production, surgical instruments, gears, valves, and tools, owing to their versatile properties and unmatchable performance.

Q: What is the process for welding Stainless Steel 420 Plates?

A: Welding these plates requires the use of special electrodes and both pre- and post-weld heating to prevent cracking and optimize joint strength, due to the grade's moderate weldability.

Q: When can I expect delivery of Stainless Steel 420 Plates after ordering?

A: Delivery time depends on the order size, customization requests, and current stock. Typically, dispatch occurs promptly after payment and procurement processing, with freight managed efficiently for timely delivery.